Low-melting point inorganic nitrate salt heat transfer fluid

ABSTRACT

A low-melting point, heat transfer fluid made of a mixture of four inorganic nitrate salts: 9-18 wt % NaNO 3 , 40-52 wt % KNO 3 , 13-21 wt % LiNO 3 , and 20-27 wt % Ca(NO 3 ) 2 . These compositions can have liquidus temperatures less than 100 C; thermal stability limits greater than 500 C; and viscosity in the range of 5-6 cP at 300 C; and 2-3 cP at 400 C.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to, and the benefit of, U.S.Provisional Patent Application Ser. No. 61/028,567 filed Feb. 14, 2008,which is herein incorporated by reference.

FEDERALLY SPONSORED RESEARCH

The United States Government has rights in this invention pursuant toDepartment of Energy Contract No. DE-AC04-94AL85000 with SandiaCorporation.

BACKGROUND OF THE INVENTION

The present invention relates generally to low-melting point inorganicnitrate salt compositions for use as heat transfer fluids and thermalenergy storage media in solar energy application, such as solarparabolic trough electrical power plant systems.

When combined with thermal energy storage (TES), a solar parabolictrough electrical power plant has the important ability to dispatchelectrical output to match peak demand periods. An important componentof TES system optimization is the choice of heat transfer fluids used inthe TES system and/or the solar field. Very large quantities (millionsof kilograms) of heat transfer fluid are required for energy storage in100-MW to 200-MW power plants and entail high capital investment costs,so minimizing that cost while maximizing the heat transfer fluidperformance is paramount.

The current generation of commercial parabolic trough plants uses amixture of organic compounds, diphenyl oxide and biphenyl, as the heattransport fluid in the collector field. This synthetic oil currentlyoffers the best combination of low freezing point (12° C.) and uppertemperature limit (393° C.) among available heat transfer fluids.However, the characteristics of this fluid have essentially set a flooron the levelized energy costs for two reasons. First, the peak allowablefluid temperature effectively limits live and reheat steam temperaturesto about 370° C., which limits the gross efficiency of the Rankinecycle. The efficiency limit sets a minimum value for the requiredcollector area per MWe of plant rating. Second, commercial solarprojects can often reduce the levelized cost of energy through theaddition of a thermal storage system. The storage system, in conjunctionwith a larger collector field, increases the annual capacity factor anddistributes the operation and maintenance costs over a larger number ofmegawatt-hours. However, a direct thermal storage system using organicoil as the storage medium is generally considered to be too expensive.

Current commercial projects must rely on an indirect storage system, inwhich thermal energy from the field is transferred to a second fluid forstorage. An indirect system entails performance penalties due to thetemperature drops associated with the transfer of energy between thecollector loop and storage as well as the cost of collection-to-storageheat exchangers. To relax the temperature and pressure limitations of asynthetic oil, a molten salt can be adopted as the heat storage fluid.These inorganic fluids offer several favorable characteristics,including upper temperature limits in the range of 500° C., lower unitcost, vapor pressures of only a few Pascals and satisfactory physicalproperties. The fluid properties allow two important advancements in thetechnology. The Rankine cycle efficiency improves, which reduces thecollector area required per MWe of plant rating and the combination oflow fluid cost and low vapor pressure allows the heat transport fluid tobe used directly as the thermal storage medium. The elimination of theoil-to-nitrate salt heat exchangers also reduces the unit storage systemcosts. Such a direct system would benefit greatly from a redesignedparabolic trough system, such as the Supertrough described by Kolb andDiver.

Sandia National Laboratories has evaluated alternative inorganic moltensalts that are inexpensive relative to organic fluids, can be used athigher temperatures of 450° C. to 500° C. or more (increasing powercycle efficiency), and have virtually no vapor pressure within operatingtemperatures and are thus amenable to use in large TES tanks. Theprimary disadvantage of most molten salt formulations is relatively highfreeze points that range from about 130° C. to 230° C. depending oncomposition as compared to about 13° C. for organic fluids. As such,considerable care must be taken to ensure salt heat transfer fluid doesnot freeze in the solar field or other system or TES piping. Despitethese engineering issues, overall evaluations for this direct moltensalt heat transfer fluid approach have been encouraging, with the mainissue being selection of a molten salt formulation with an acceptablefreeze point as well as high temperature durability.

Several molten salt heat transfer fluids have been used for solarthermal systems. The binary Solar Salt mixture was used at the 10 MWeSolar Two central receiver project in Barstow, Calif. It will also beused in the indirect TES system for the Andasol plant in Spain. Amongthe candidate mixtures, it has the highest thermal stability and thelowest cost, but also the highest melting point. Hitec HTS® has beenused for decades in the heat treating industry. This salt is thermallystable at temperatures up to 454° C., and may be used up to 538° C. forshort periods, but a nitrogen cover gas is required to prevent the slowconversion of the nitrite component to nitrate. The currently availablemolten salt formulations do not provide an optimum combination ofproperties, freezing point, and cost that is needed for a replacementheat transfer fluid in parabolic trough solar fields. Therefore, thework summarized in this report sought to develop an heat transfer fluidthat will better meet the needs of parabolic trough plants.

Table 1 compares the liquidus temperatures (liquid-solid phasetransition temperature) of a number of molten nitrate salt mixtures.Inspection of published phase diagrams revealed that ternary mixtures ofNaNO₃ and KNO₃ with several alkali and alkaline earth nitrates havequite low melting points. The eutectic of LiNO₃, NaNO₃ and KNO₃ melts at120° C., while a mixture of Ca(NO₃)₂, NaNO₃ and KNO₃ melts at about 133°C. Several eutectic systems containing three constituents are liquids aslow as 52° C. Unfortunately, melts containing ammonium nitrate decomposeat a low temperature and those containing silver nitrate would beprohibitively expensive.

No phase diagrams appear to exist for mixtures of molten nitrate saltscontaining more than three constituents that would identify those havinglower liquidus temperatures than the mixtures listed in Table 1. Astraightforward approach to identifying an improved heat transfer fluidwould be to add constituents to solar nitrate salt that depress themelting point significantly without compromising its properties.Metallic nitrates are obvious choices because of their miscibility andpotential stability in contact with air. The thermodynamic criteria formelting point depression by additions of a second constituent have beensummarized by Stolen and Grande. Constituents of systems whose phasediagrams that display eutectic behavior satisfy the thermodynamiccriteria, while those that display peritectic behavior do not. Althoughthe activity coefficients for all the mutual combinations of the alkalimetal nitrates and alkaline earth nitrates are not available, we expectthat such criteria will be satisfied by additions of calcium nitrate andlithium nitrate to sodium nitrate and potassium nitrate because allbinary combinations of these nitrate salts display melting pointdepression, as well as eutectics, as do the ternary systems.

TABLE 1 Comparison of liquidus temperatures of various molten nitratesalt mixtures. Compositions are given as mol %, cation basis.Temperature data were obtained from Phase Diagrams for Ceramistspublished by American Ceramic Society/NIST. Liquidus Na K Ca Li NH₄Other Temp. mol % mol % mol % mol % mol % mol % ° C. Notes 50 50 221Na—K—NO₃ eutectic 66 34 238 Binary Solar Salt (60-40, by wt.) 7 44 49  141 Hitec ® HTS NaNO₂ 21 49 30 133 Ca—Na—K—NO₃ eutectic 18 52 30 120Li—Na—K—NO₃ eutectic 58 11 31 117 Ca—Li—K—NO₃ eutectic 19.3 29.4 51.3 92Poor thermal stability due to NH4NO3 20.7 60.2 19.1 52 Lowest meltingAgNO₃ mixture identified in literatureIn this work, we investigated common-anion additions to NaNO₃—KNO₃mixtures (binary Solar Salt) as a means to identify low melting (lowliquidus temperature) mixtures. We evaluated the properties ofmulti-component molten nitrate salt mixtures as alternative heattransfer and storage fluids for a parabolic trough system. We wereparticularly interested in the chemical stability and viscosity ofmulti-component mixtures that display significantly lower melting pointsthan Solar nitrate salt. The necessary chemical stability data regardingmulti-component mixtures of alkali and/or alkaline earth nitrates wereobtained experimentally.

Of course, improved molten salt compositions will be useful for a widerange of industrial process heat applications, in addition to solarthermal heat transfer and thermal energy storage systems.

SUMMARY OF THE INVENTION

A low-melting point, heat transfer fluid made of a mixture of fourinorganic nitrate salts including 9-18 wt % NaNO₃, 40-52 wt % KNO₃,13-21 wt % LiNO₃, and 20-27 wt % Ca(NO₃)₂. These compositions can haveliquidus temperatures less than 100 C; thermal stability limits greaterthan 500 C; and viscosity in the range of 5-6 cP at 300 C; and 2-3 cP at400 C.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and form part ofthe specification, illustrate various examples of the present inventionand, together with the detailed description, serve to explain theprinciples of the invention.

FIG. 1 shows the nitrite concentrations in quaternary molten nitratesalts at chemical equilibrium with air, compared to binary Solar Salt.

FIG. 2 shows the viscosity of quaternary molten nitrate salts, comparedto the ternary lithium-sodium-potassium nitrate salt.

DETAILED DESCRIPTION OF THE INVENTION

A heat transfer fluid (HTF) for use at elevated temperatures wasformulated by combining sodium nitrate, potassium nitrate, lithiumnitrate and calcium nitrate. The key properties that are provided by theparticular range of compositions determined experimentally are lowsolidification point, stability at high temperature, stability incontact with air, low viscosity, low cost, non-corrosive to typicalcontainer materials, low vapor pressure and high heat capacity. The heattransfer liquid may be used for heat collection and transfer; andthermal energy storage in solar energy systems, among otherapplications. A new formulation of molten nitrate salts will first andforemost provide a heat transfer fluid that has a lower freezing pointthan is currently available from any molten salt mixture of inorganicnitrate and/or nitrite salts available commercially. A solid phase willnot form in these mixtures until the temperature is below 100° C. Thisallows the HTF to be used in applications in which the expensiveparasitic energy costs necessary for freeze protection can besignificantly reduced. As a specific example, this new HTF will enhancethe value of energy delivered from parabolic trough solar energy plantsbecause the cost of operating and maintaining the solar system will besignificantly lower with a molten salt formulation that freezes at thelower temperatures. The new formulations are sufficiently stable at hightemperature that it will increase the upper temperature limits of theHTF in the solar field operating environment compared to the syntheticoils currently used as HTF. The higher operating temperature limitsignificantly increases power cycle efficiency and overall power plantsun-to-net electric efficiency.

Existing technology for inorganic molten salt HTF is based on either2-component mixtures of sodium nitrate and potassium nitrate or3-component mixtures of the preceding salts with calcium nitrate. Thenew formulation is technically different in that it consists of afour-component mixture using lithium nitrate in combination with theabove. However, the simple combination of arbitrary proportions of thesefour nitrate salts will not result in a mixture that begins to solidifyat a temperature of interest for HTF applications and solar thermalenergy systems in particular.

The range of compositions that combine four inorganic nitrate salts, andare suitable for the purpose of solar energy applications, include:

Range of Compositions (wt %)

-   -   9-18 wt % NaNO₃,    -   40-52 wt % KNO₃,    -   13-21 wt % LiNO₃, and    -   20-27 wt % Ca(NO₃)₂        Note that these compositions can be either specified in Mole %        (Mol %), or in Weight % (wt %).        Specific compositions were made and tested:

Composition “QA” (Mol %, Cation Basis)

-   -   16 mol % NaNO₃,    -   47 mol % KNO₃,    -   25 mol % LiNO₃, and    -   12 mol % Ca(NO₃)₂.        Composition “QA” is mostly liquid at 96.7 C.

Composition “QB” (Mol %, Cation Basis)

-   -   20 mol % NaNO₃,    -   38 mol % KNO₃,    -   31 mol % LiNO₃, and    -   12 mol % Ca(NO₃)₂        Composition “QB” has a liquid phase at 96.7 C, but less liquid        than Composition #1 at that temperature.

Composition “QC” (Mol %, Cation Basis)

-   -   11 mol % NaNO₃,    -   50 mol % KNO₃,    -   27 mol % LiNO₃, and    -   12 mol % Ca(NO₃)₂

Composition “#4” (Mol %, Cation Basis)

-   -   14 mol % NaNO₃,    -   49 mol % KNO₃,    -   20 mol % LiNO₃, and    -   17 mol % Ca(NO₃)₂

These new molten salt compositions (formulations) have improvedproperties compared to the oil-based HTF currently used in solar powerplants. First, the molten salt costs significantly less. Second, themolten salt is relatively benign in terms of environmental impact,whereas the oil is toxic and carries cleanup and waste disposalpenalties when leaks occur. Third, the molten salt has a higher densityand heat capacity, requiring lower flows, much lower pressure drops inthe system piping (which reduces pumping costs) and enhanced heattransfer capability. Fourth, the molten salt HTF allows a higheroperating temperature differential in the solar field and greatertemperature gradients in thermal storage systems which greatly enhancesefficiency and thermal storage utilization. Fifth, the molten salt canbe operated at higher temperatures which, as noted above, leads tohigher power cycle and power plant efficiencies. Six, molten salt hasvirtually no inherent vapor pressure, which allows its use in thermalenergy storage tanks that are vented to atmosphere versus usinghigh-cost pressure vessels that would be required for other HTF types.Seven, the molten salt HTF is stable in contact with air and is notflammable.

The new formulation is a physical mixture of constituents that arecompletely miscible in the molten state in all proportions. The range ofproportions of the constituents that will optimize the desiredproperties of an HTF (freezing point, upper stability temperature, cost,low viscosity) is relatively narrow, and is not obvious based uponexisting information regarding the phase diagrams of many ternarysystems of alkali and alkaline earth nitrates have been published. Nophase diagrams for quaternary (four-component) molten salt mixtures ofsuch constituents were discovered during a search of the literature viaon-line resources or hard copies of phase diagram handbooks. Althoughadditions of soluble constituents to molten salts having a common aniontypically depress the freezing point of such mixtures, this is notnecessarily the case for multi-component mixtures. Furthermore, thethermodynamic database that would allow predictions of phase behaviorbased on the composition of multi-component mixtures is virtuallynon-existent and thus not suitable for accurate calculations of phasestability. For this reason, the composition required to achieve thelowest-melting mixture is not obvious, and must be determined byexperiments using a range of molten salt compositions.

EXPERIMENTAL RESULTS

The quaternary molten salt mixtures were prepared from NaNO₃, KNO₃,LiNO₃ and Ca(NO₃)₂-tetrahydrate Reagent Grade salts (Sigma-Aldrich Co.,St. Louis, Mo.). To melt small quantities of the nitrate mixtures forobservations of solidification behavior and viscosity measurements,weighed-amounts of the individual salts were loaded into high-purityalumina crucibles and were heated in small furnaces open to theatmosphere. The temperature was initially maintained at approximately150° C. to allow the water of hydration of the calcium nitrateconstituent to evolve slowly. After visual indications of vaporevolution ceased, the melts were heated to 350° C. to 400° C.,periodically stirred, and maintained at an elevated temperature for atleast one overnight period before cooling and sub-dividing for propertydeterminations.

Chemical stability tests were performed by melting several kilograms ofmolten salt mixtures in stainless steel crucibles that were equippedwith gas dispersion tubes. The melts were heated to successively highertemperatures, up to at least 520° C., and kept at each constanttemperature for several days as dry air was bubbled through the melt.Salt samples were removed at each temperature increment for chemicalanalysis. The nitrite (NO₂—) concentration was assayed by HachAnalytical Method 8153 using a Hach Co. (Loveland, Colo.) DR2010UV-VISspectrometer.

The liquidus temperature, at which solidification begins, was determinedfor a range of multi-component molten nitrate salt compositions.Approximately 10 grams of the salt mixtures were placed in Pyrex testtubes which were housed in several recesses in a large aluminum block todampen temperature fluctuations. The assembly was heated in an oven andtemperatures were progressively lowered from about 20° C. above theliquidus point until a small amount of a solid phase was observed in aparticular tube. The corresponding liquid phase was sampled and analyzedto determine the cation ratios of the residual liquid. Each temperaturestage was maintained for at least several days and typically for a weekor longer at temperatures below 100° C. In some tests, an alumina chipwas added to assure nucleation sites were present for solidification.

The viscosities of numerous molten salt mixtures were measured using aBrookfield DV-II+ viscometer (Brookfield Engineering, Middleboro,Mass.). The molten salt mixtures were contained in a stainless steeltube that was heated in a small furnace at constant temperaturemaintained by a Brookfield Thermosel controller. Viscosities weremeasured by increasing the temperature sequentially from a startingtemperature about 10° C. to 20° C. above the liquidus to a maximum ofapproximately 220° C., then successively decreasing the temperature tore-determine values for repeatability. The molten salt was maintained ateach temperature sufficiently long for a steady state to be attained andthe viscosity to indicate a constant value. The viscometer configurationwas limited to about 10 cP at the low end of measured values. However,despite the limited accuracy of low viscosity measurements, it wasadequate to compare the effect of the constituents of the molten saltmixtures on viscosity.

An important property of the quaternary molten salt formulations is theliquidus temperature, at which a solid phase is formed by a particularcomposition. For binary mixtures of alkali metal nitrates and alkalinemetal nitrates, the minimum liquidus temperature is typically a eutecticpoint. Ternary phase diagrams of molten nitrates are typically morecomplex than simple eutectic systems. The phase behavior ofmulti-component mixtures of nitrate salts is likely to be even morecomplex, as well as difficult to represent graphically.

Three different mixtures of the four nitrate salts were identified thatdisplay liquidus temperatures less than 100° C. These quaternarymixtures are designated QA, QB and QC, and are composed of theproportions of constituents as given in Table 2. All of the fourconstituent nitrate salts must be present in significant proportions tocreate a low-melting mixture, based on those evaluated to date. Liquidustemperatures for several such mixtures are collected in Table 2 and arecompared with published values for several binary and ternary nitratemixtures.

TABLE 2 Liquidus temperatures of multi-component molten nitrate saltmixtures. Compositions are given as mol %, cation basis. Na K CaLiquidus mol mol mol Li Temp. % % % mol % ° C. Notes 50 50 221 Na—K—NO₃eutectic 21 49 30 133 Ca—Na—K—NO₃ eutectic 18 52 30 120 Li—Na—K—NO₃eutectic 58 11 31 117 Ca—Li—K—NO₃ eutectic 20 38 12 31 <95 QA 16 47 1225 <95 QB 11 50 12 27 <95 QC

Computational molecular dynamics methods are in progress to identifyminimum liquidus compositions and provide directions within thefour-dimensional composition space that indicates lower liquidustemperatures.

Chemical Stability of Molten Salts

It is essential that low-melting molten salt mixtures be sufficientlystable at high temperature to realize any advantages in a solar thermalenergy system. The primary aspects of molten nitrate salt chemistry thatare relevant to solar thermal applications are the primary equilibriumchemistry and the reactions by which the molten salts interact withatmospheric gases such as carbon dioxide. The chemical equilibrium ofthe binary Solar salt mixture has been studied at high temperature andthe mixture is quite stable up to 600° C. The primary reaction is thepartial dissociation of nitrate ion (NO₃ ⁻) to nitrite ion (NO₂ ⁻) andoxygen, as shown by Equation 1. The shift from nitrate to nitrite occursslowly and is limited by the partial pressure of oxygen in theatmosphere contacting the molten salt. The equilibrium constant for thenitrate dissociation reaction, K₁, is given by Equation 2, in which themolal concentrations of the anions and the partial pressure of oxygenrepresent the thermodynamic activities of the compounds.NO₃ ⁻=NO₂ ⁻+½O₂  (1)K₁=[NO₂ ⁻](P,O₂)^(1/2)/[NO₃ ⁻]  (2)

Nissen and Meeker measured the equilibrium constant for an equimolarmixture of NaNO₃ and KNO₃. The equilibrium shift of the equimolarmixture results in 1.1 mol % (anion basis) nitrite at 500° C. and 5.7mol % at 600° C. in contact with air. The nitrite shift behavior ofternary molten nitrate salts containing either calcium nitrate orlithium nitrate additions to binary mixtures of NaNO₃ and KNO₃ has beenshown to follow Equations 1 and 2. The values of the equilibriumconstant depend somewhat upon the particular composition of the mixturebut are comparable to that of binary Solar Salt.

The equilibrium concentrations of nitrite ion in several quaternarynitrate salt mixtures were measured between temperatures of 450° C. and510° C. The results are plotted in FIG. 1, which shows ppm by weight ofnitrite ion versus temperature in a semi-log format. The four-componentmolten salts, having the compositions designated QA, QB and QC, as givenin Table 2. The line indicates the behavior of binary Solar Salt. Theconcentration of nitrite in the quaternary mixtures is somewhat less,but basically comparable, to that calculated for the binary Solar Saltat corresponding temperatures. The Na—K—Li nitrate eutectic mixture(shown as filled diamond symbols) was also studied and the resultsconfirmed measurements made in an earlier study. The chemicalequilibrium data follow the same trend with temperature as Solar Salt,which indicates that the enthalpy of the controlling chemical process iseffectively the same, i.e., reaction (1).

Because the equilibrium concentration of nitrite is less than onepercent at the proposed maximum operating temperatures of solar troughsystems, molten salts, which contain substantial concentrations ofnitrite, such as Hitec HTS, must be protected from contact with air.Such contact gradually reverses reaction (1), thereby decreasing thenitrite level and consequently increasing the melting point. Low-meltingmolten salts containing significant amounts of nitrite that may beidentified by future experimental studies would require a systemdesigned to minimize or avoid contact with air. Such systems are withinthe design envelope of a trough receiver system.

Nitrite ions, as well as nitrate ions, may decompose at sufficientlyhigh temperature to yield several types of oxide ion species, e.g.,oxide, peroxide and superoxide. A generalized decomposition reaction ofnitrite is given by Equation 3, in which oxide ion formation isaccompanied by evolution of nitrogen oxides. Carbon dioxide in theatmosphere has a marked effect on the concentrations of oxide ionspecies in nitrate melts. Carbon dioxide in air will convert oxide ionsto carbonate, according to Equation 4.2NO₂→O⁻²+NO_(x)(several species)  (3)CO₂+O⁻²=CO₃−2  (4)

The solubility of carbonate ion in binary Solar Salt is approximately 5mol % near the eutectic point. Such a high solubility presents littleconcern for a heat transfer and storage system because an extremely longtime would be required to absorb enough CO₂ from the atmosphere tosaturate a large mass of molten salt. However, no phase diagrams areavailable for multi-component systems to indicate the solubility ofcarbonate. Solubility of carbonate appears to be significantly less inmulti-component nitrate mixtures containing calcium nitrate. A solidphase was observed at high temperature in molten ternary mixtures ofNaNO₃, KNO₃ and Ca(NO₃)₂, at temperatures from 500° C. to about 540° C.,depending on the proportion of calcium nitrate present. These melts werecontacted for several days with air by a bubbler to enhance theinteraction of the molten salt with carbon dioxide. Chemical analysis ofsalt samples identified the presence of carbonate ions. Theconcentration of dissolved carbonate ions increased with temperature butsaturation levels were not determined.

An important consequence of decomposition reactions with regard to usinga molten nitrate salt mixture as a heat transfer fluid is that insolubleproducts may form, which tend to plug valves, pipes and heat transfersurfaces. Another effect is that the soluble oxide ions aggravatecorrosion at high temperatures. The use of nitrate molten salts for heattransfer or storage at high temperature is limited by reactions (3) and(4). Observations regarding the appearance of a solid phase inmulti-component molten salt mixtures are collected in Table 3. Thequaternary mixtures gave visible indications of solid phases afterseveral days at 520° C. accompanied by CO₂ bubbling. This material was asmall fraction of the melt and was not amenable to sampling in theexperimental apparatus used. In contrast, the ternary Li—Na—K-nitratemelt did not demonstrate any solid phases after similar periods at 540°C., which agrees with behavior reported in previous experiments Itappears that the quaternary nitrate mixtures are chemically stable attemperatures of nominally 500° C. The chemical stability is beingfurther evaluated during prolonged testing.

TABLE 3 Approximate thermal stability limits of selected molten nitrateand nitrate-nitrite salt mixtures. Compositions are given as mol %,cation basis. The temperature values refer to melts in contact with airexcept for Hitec. Na K Ca Maximum mol mol mol Li Other Temp. % % % mol %mol % ° C. Notes 66 34 — — 600 Binary Solar Salt (60-40, by weight) 7 44— — 49 450 to Hitec ® HTS NaNO₂ 538 (N₂ cover gas) 18 45 37 550 Ref. 1230 50 20 — 505 Ref. 12 20 50 30 — 480 Ref. 12 20 38 12 31 ~520  QA 16 4712 25 ~520  QB 11 50 12 27 ~520  QC 18 45 — 37 >540  Li—Na—K-NitrateeutecticViscosity of Molten Salts

The physical properties of heat transfer fluids, viscosity, density,heat capacity and thermal conductivity, are needed to performengineering design calculations of trough collector and storage systems.Viscosity is particularly important because it strongly influencespumping costs in a distributed system with extended piping runs, such asa trough receiver plant. The viscosity of a number of molten saltmixtures were measured to determine the effects of the variousconstituents. FIG. 2 presents an Arrhenius plot of viscositymeasurements for the same quaternary molten salt mixtures that werediscussed in the preceding section on chemical stability. This plot alsocontains data for the Li—Na—K-nitrate eutectic, which freezes at 120°C., for comparison.

Calcium nitrate additions to the multi-component molten saltssignificantly increase the viscosity. This result has been reportedpreviously for binary mixtures of calcium nitrate and potassium nitrate.The viscosity near the liquidus temperature was approximately 200 cP,which is not an unreasonable value for handling in a TES system. Theviscosity at temperatures in the median range of normal operation of atrough system, e.g., 300° C., is approximately 5-6 cP and is 2-3 cP at400° C., as determined by extrapolating the data from the measurabletemperature range. Melts that contain appreciable calcium nitrate alsodisplay curvature in an Arrhenius plot in contrast to the linear slopeof the calcium-free ternary melt. Such behavior has been reported anddiscussed by Rhodes and co-workers.

The experimental results generally agree with published studies to theextent that the compositions of the molten salts can be compared withintheir respective liquid-phase temperature ranges. Calciumnitrate-containing molten salts tend to form glassy, viscous melts nearthe freezing temperature while lithium nitrate appears to have a minoreffect on the viscosity of mixtures. Further development studies willdetermine how to adjust the proportions of the constituents of aquaternary molten salt to minimize the low-temperature viscosity, whileoptimizing other fluid properties and cost.

Cost of Constituents

Current cost data for commodity quantities of the individual nitrateconstituents have not yet been obtained. However, the relative cost ofthe constituents is expected to follow the ranking,calcium<sodium<potassium<lithium, based on a recent paper by Hoshi, etal. This ranking is basically the same as that determined a number ofyears ago by a study of ternary molten nitrate salts for solar centralreceiver systems. The previous study also considered that lithiumnitrate may be more economical to prepare in large quantities byconverting from lithium carbonate with nitric acid. The unit price oforganic heat transfer oils is nominally $3 per kilogram, while acommercial storage system will probably require a unit medium cost nohigher than about $0.50-$1.00 per kilogram. Thus, organic fluids arerelatively expensive and the cost of a low-melting mixture of nitratesalts will be significantly less.

With the objective of producing four-component molten salt mixtures thathave liquidus temperatures less than 100° C., the cost of theseconstituent salts will be very important to determine. These costsinfluence the strategy of blending the constituents to achieve theoptimal mix of properties versus cost. Although calcium nitrate is thelowest cost constituent, it produces mixtures that have relatively highviscosity. In addition, the effect on thermal stability of mixtures issuch that calcium nitrate is the least favored constituent. Lithiumnitrate is the most expensive constituent but has only a modest effectof reducing the maximum useable temperature of a molten salt mixture, asdiscussed above.

We have identified a class of quaternary molten salt compositions, basedon solar nitrate salt, that display much lower liquidus temperatures andthat may be useful as heat transfer fluids for solar thermal energysystems. These molten salt mixtures contain calcium nitrate and lithiumnitrate to depress the melting point of a salt mixture based on sodiumnitrate and potassium nitrate. We established the working temperatureranges of these mixtures experimentally and determined the viscosity atthe low temperature range of these molten salts. At the limiting maximumtemperature, instability was manifested by the appearance of solidphases. However, it appears to be feasible to use these quaternarymixtures at maximum temperatures of 500° C. Although viscosity isconsiderably higher than binary Solar Salt, it does not preclude usingthe molten salts at a low temperature. Cost estimates are qualitative atthis point, although these molten salt mixtures are expected to berelatively inexpensive compared to organic heat transfer fluids, thusmaking them amenable for use in large-scale thermal energy storagesystems. Experimental studies are currently in progress to fullyevaluate and optimize the physical and chemical properties of thesemolten nitrate salts.

Table 4 lists specific samples of quaternary nitrate salts (in mol %,cation basis), that were prepared in the laboratory.

TABLE 4 Compositions of sample quaternary nitrate salts (mol %, cationbasis). NaNO₃ KNO₃ LiNO₃ Ca(NO₃)₂ Sample (Mol %) (Mol %) (Mol %) (Mol %)1 28 29 26 16 2 29 28 16 26 3 30 30 30 10 4 31 32 31 6 5 20 38 30 12 616 47 27 10 7 17 50 29 5 8 15 45 27 8 9 9 36 30 10 10 17 43 35 5 11 1641 32 10 12 20 38 30 12 13 21 40 27 12 14 18 37 33 12 15 19 39 27 15 1615 45 25 15 17 15 52 22 11 18 12 49 18 11

The particular examples discussed above are cited to illustrateparticular embodiments of the invention. Other applications andembodiments of the apparatus and method of the present invention willbecome evident to those skilled in the art. It is to be understood thatthe invention is not limited in its application to the details ofconstruction, materials used, and the arrangements of components setforth in the following description or illustrated in the drawings.

The scope of the invention is defined by the claims appended hereto.

1. The composition comprising in Mol %, cation basis: 16 mol % NaNO₃, 47 mol % KNO₃, 25 mol % LiNO₃, and 12 mol % Ca(NO₃)₂.
 2. The composition of claim 1, wherein the liquidus temperature is less than 100° C.
 3. The composition of claim 1, wherein the thermal stability limit is greater than 500° C.
 4. The composition of claim 1, wherein the viscosity is 5-6 cP at 300 C; and is 2-3 cP at 400° C.
 5. The composition comprising in Mol %, cation basis: 20 mol % NaNO₃, 38 mol % KNO₃, 30 mol % LiNO₃, and 12 mol % Ca(NO₃)₂.
 6. The composition comprising in Mol %, cation basis: 11 mol % NaNO₃, 50 mol % KNO₃, 27 mol % LiNO₃, and 12 mol % Ca(NO₃)₂.
 7. The composition consisting essentially of in Mol %, cation basis: 16 mol % NaNO₃, 47 mol % KNO₃, 27 mol % LiNO₃, and 10 mol % Ca(NO₃)₂.
 8. The composition of claim 7, wherein the liquidus temperature is less than 100° C.
 9. The composition of claim 7, wherein the thermal stability limit is greater than 500° C.
 10. The composition of claim 7, wherein the viscosity is 5-6 cP at 300 C; and is 2-3 cP at 400° C.
 11. The composition consisting essentially of in Mol %, cation basis: 20 mol % NaNO₃, 38 mol % KNO₃, 30 mol % LiNO₃, and 12 mol % Ca(NO₃)₂.
 12. The composition consisting essentially of in Mol %, cation basis: 11 mol % NaNO₃, 50 mol % KNO₃, 27 mol % LiNO₃, and 12 mol % Ca(NO₃)₂.
 13. A composition, comprising in Mol %, cation basis: 14 mol % NaNO₃, 49 mol % KNO₃, 20 mol % LiNO₃, and 17 mol % Ca(NO₃)₂. 